Аннотация: Rubidium neodymium dimolybdate, RbNd(MoO4)(2), microcrystals have been fabricated by solid state synthesis at T=550-600 degrees C by t=324 ks. Crystal structure of RbNd(MoO4)(2) has been refined by Rietveld method in space group Pbcn with cell parameters a = 5.1772(1) angstrom, b = 18.7293(4) angstrom, and c = 8.2774(1) angstrom (R-B=5.05%). The crystal structure of RbNd(MoO4)(2) consists of layers of MoO4 tetrahedrons cornersharing with NdO8 square antiprisms. These layers are perpendicular to b-axis of the unit cell. About 20 narrow Raman lines have been observed in Raman spectrum recorded for RbNd(MoO4)(2) powder sample. (C) 2010 Elsevier B.V. All rights reserved.
WoS,
Scopus,
Смотреть статью,
Для получение полного текста обратитесь в библиотеку
Доп.точки доступа:
Atuchin, V. V.; Chimitova, O. D.; Gavrilova, T. A.; Molokeev, M. S.; Молокеев, Максим Сергеевич; Kim, S. J.; Surovtsev, N. V.; Bazarov, B. G.; Базаров Б.Г.; Bazarova, Zh.G.; Базарова Ж.Г.; International Conference on Crystal Growth(16 ; 2010 ; Aug. ; 08-13 ; Beijing, China); International Conference on Vapor Growth and Epitaxy(14 ; 2010 ; Aug. ; 08-13 ; Beijing, China)