/ D. A. Balaev [et al.] // Phys. Solid State. - 2013. - Vol. 55, Is. 7. - P. 1401-1406, DOI 10.1134/S1063783413070056. - Cited References: 18. - This study was supported by the Russian Foundation for Basic Research (project no. 12-03-90839-mol_rf_nr) and the Ministry of Education and Science of the Russian Federation (agreement no. 8429). . - ISSN 1063-7834РУБ Physics, Condensed Matter

Аннотация: The structural, microstructural, and magnetic properties of aluminum-manganese oxide in the ratio Mn: Al = 1: 1 in the well-crystallized and nanoheterogeneous states have been investigated. This oxide is obtained under various thermal treatment conditions and at different partial pressures of oxygen. The composition and cation distribution of the manganese and aluminum ions in spinel sites are determined. It is shown that the studied compound is a ferrimagnet with the Curie point T (C) a parts per thousand 26 K.

Смотреть статью,
WoS,
WOS,
Для получение полного текста обратитесь в библиотеку

Держатели документа:
Russian Acad Sci, Siberian Branch, LV Kirensky Phys Inst, Krasnoyarsk 660036, Russia
Russian Acad Sci, Siberian Branch, Boreskov Inst Catalysis, Novosibirsk 630090, Russia
Novosibirsk State Univ, Novosibirsk 630090, Russia

Доп.точки доступа:
Balaev, D. A.; Балаев, Дмитрий Александрович; Bulavchenko, O. A.; Dubrovskii, A. A.; Дубровский, Андрей Александрович; Tsybulya, S. V.; Cherepanova, S. V.; Gerasimov, E. Y.; Shaikhutdinov, K. A.; Шайхутдинов, Кирилл Александрович

/ S. S. Aplesnin [et al.] // Ceram. Int. - 2016. - Vol. 42, Is. 4. - P. 5177-5183, DOI 10.1016/j.ceramint.2015.12.040. - Cited References: 45. - This work was supported by the Russian Foundation for Basic Research Projects no. 15-42-04099 r_siberia_a, Siberian Branch of Science and NAS of Belarus “Electronic and magnetic phase transitions in materials with magnetoelectric affect” and government work no. 114090470016. . - ISSN 0272-8842РУБ Materials Science, Ceramics

Аннотация: Infrared absorption spectra of the bismuth pyrostannate Bi2(Sn0.95Cr0.05)2O7 were investigated in the frequency range 350-1100 cm-1 at temperatures of 110-525 K. Four frequency regions with split absorption lines are distinguished. Softening of frequencies at the structural transitions was observed. The maxima of permittivity measured in the frequency range 1-200 kHz at temperatures 100-400 K were determined. It was found that the magnetic susceptibility changes its sign in the low-temperature region. The correlation between anomalies in the magnetic susceptibility, permittivity, and absorption line intensity was established. Softening of frequencies is explained by the variation in the coefficient of thermal expansion of the lattice. The temperature behavior of permittivity is described using the Debye model. © 2015 Elsevier Ltd and Techna Group S.r.l.

Смотреть статью,
Scopus,
WOS,
Для получение полного текста обратитесь в библиотеку

Держатели документа:
Kirensky Institute of Physics, Russian Academy of Sciences, Siberian Branch, Akademgorodok 50, Krasnoyarsk, Russian Federation
Siberian State Aerospace University, Krasnoyarsk, Russian Federation

Доп.точки доступа:
Aplesnin, S. S.; Аплеснин, Сергей Степанович; Udod, L. V.; Удод, Любовь Викторовна; Sitnikov, M. N.; Shestakov, N. P.; Шестаков, Николай Петрович