Аннотация: The phase transformation behavior of a single-phase tetragonal Sr0.8Gd0.2CoO3-δ (with ordered distribution of Sr2+/Gd3+ cations and anion vacancies) was investigated by TG–DSC and XRD at 1100–1473 K and oxygen partial pressure p(O2) from 1 to 5·104 Pa. The first-order smeared order-disorder (o-d) phase transition involving heat absorption was observed at about 1383 K under O2-Ar flow with p(O2) > 2.5 kPa. The crystal structure of the high-temperature phase was found to be cubic perovskite with disordered Sr2+/Gd3+ cations and anion vacancies. The temperature of o-d transition at p(O2) > 2.5 kPa was not influenced by the heating rate or oxygen partial pressure. It was shown that at p(O2) < 2.5 kPa the o-d transition gives rise to Sr0.8Gd0.2CoO3−δ decomposition to form CoO and Sr2.4Gd0.6Co2O7-δ − Ruddlesden-Popper type phase with novel composition. The phase boundaries between the ordered tetragonal Sr0.8Gd0.2CoO3−δ, disordered cubic Sr0.8Gd0.2CoO3−δ and CoO + Sr2.4Gd0.6Co2O7-δ composite as a function of temperature and p(O2) values were determined.
Смотреть статью,
WOS,
Для получение полного текста обратитесь в библиотеку
Держатели документа:
Inst Chem & Chem Technol, Krasnoyarsk 660036, Russia.
Kirensky Inst Phys, Krasnoyarsk 660036, Russia.
Доп.точки доступа:
Vereshchagin, S. N.; Dudnikov, V. A.; Дудников, Вячеслав Анатольевич; Shishkina, N. N.; Solovyov, L. A.; Russian Foundation for Basic Research, Government of Krasnoyarsk Territory, Krasnoyarsk Region Science and Technology Support Fund [16-43-240505 p_a, 16-02-00507A]