Перевод заглавия: Термитный синтез и исследование ферромагнитных нанокомпозитных тонких пленок Co-ZrO2
Рубрики:
SOLID-STATE SYNTHESIS
PHASE-FORMATION
ZrO2
NANOPARTICLES
TRANSPORT
OXIDE
MICROSTRUCTURE
NANOTHERMITE
FABRICATION
PARTICLES
Кл.слова (ненормированные):
Thermite reactions -- Reactive films -- Ferromagnetic nanocomposite films -- ZrO2
SOLID-STATE SYNTHESIS
PHASE-FORMATION
ZrO2
NANOPARTICLES
TRANSPORT
OXIDE
MICROSTRUCTURE
NANOTHERMITE
FABRICATION
PARTICLES
Кл.слова (ненормированные):
Thermite reactions -- Reactive films -- Ferromagnetic nanocomposite films -- ZrO2
Аннотация: Co-ZrO2 ferromagnetic nanocomposite thin films were successfully synthesized using a new thermite reaction between Zr and Co3O4 in layer geometry. The initial Zr/Co3O4 bilayers were obtained by the deposition of Zr layers onto Co3O4 films at room temperature. The process of mixing at the Zr/Co3O4 interface and synthesis of fine-crystalline Co and amorphous ZrO2 phases started at a temperature above the initiation temperature Tin ∼250 °C which did not depend on the bilayer thickness. For the bilayer thickness more than 300 nm high-temperature fcc-Co and cubic c-ZrO2 (or tetragonal t-ZrO2) phases were formed. For the bilayer thickness less than ∼50 nm stable low-temperature hexagonal hcp-Co and monoclinic m-ZrO2 phases were also present in the reaction product. A partial transformation from Co3O4 to CoO occurred after annealing at 300 °C. The secondary reaction between CoO and Zr started soon after Co3O4 had been converted to the CoO phase. After annealing at 500 °C more than 80% of Co was reduced and the final product contained Co nanoparticles above and below the superparamagnetic critical size embedded into a dielectric ZrO2 matrix. The synthesized Co-ZrO2 nanocomposite films possessed soft magnetic behavior, high magnetization and good chemical stability.
Смотреть статью,
Scopus,
WOS,
Для получение полного текста обратитесь в библиотеку
Держатели документа:
Kirensky Institute of Physics, Russian Academy of Sciences, Siberian Branch, Krasnoyarsk, Russian Federation
Reshetnev Siberian State Aerospace University, Krasnoyarsk, Russian Federation
Siberian Federal University, Krasnoyarsk, Russian Federation
Institute of Chemistry and Chemical Technology, Russian Academy of Sciences, Siberian Branch, Krasnoyarsk, Russian Federation
Доп.точки доступа:
Myagkov, V. G.; Мягков, Виктор Григорьевич; Zhigalov, V. S.; Жигалов, Виктор Степанович; Bykova, L. E.; Быкова, Людмила Евгеньевна; Zharkov, S. M.; Жарков, Сергей Михайлович; Matsynin, A. A.; Мацынин, Алексей Александрович; Volochaev, M. N.; Волочаев, Михаил Николаевич; Tambasov, I. A.; Тамбасов, Игорь Анатольевич; Bondarenko, G. N.; Бондаренко, Галина Николаевна