/ T. S. Spiridonova, S. F. Solodovnikov, M. S. Molokeev [et al.]> // J. Solid State Chem. - 2022. -
Vol. 305. - Ст. 122638,
DOI 10.1016/j.jssc.2021.122638. - Cited References: 71. - This research was supported by the Ministry of Science and Higher Education of the Russian Federation , projects No. 0273-2021-0008 (Baikal Institute of Nature Management, SB RAS), and No. 121031700313-8 (Nikolaev Institute of Inorganic Chemistry, SB RAS), as well as partial financial support from the Russian Foundation for Basic Research (project No. № 20-03-00533)
. - ISSN 0022-4596
Перевод заглавия: Синтез, кристаллическая структура и свойства новых ацентрических соединений Rb7Ag5–3xSc2+x(XO4)9 (X = Mo, W), родственных глазериту
Аннотация: The subsolidus phase equilibria in the system Ag2MoO4–Rb2MoO4–Sc2(MoO4)3 were studied and two new triple molybdates, Rb9Ag3Sc2(MoO4)9 and Rb7Ag5Sc2(MoO4)9, were found. The structures of Rb7Ag5Sc2(MoO4)9 and isostructural Rb7Ag5Sc2(WO4)9 of the Cs7Na5Yb2(MoO4)9 type (the space group R32) were determined. The found composition of the triple tungstate crystal, Rb7Ag4.61Sc2.13(WO4)9, indicates a non-stoichiometric compound formula, Rb7Ag5–3xSc2+x(WO4)9. Both structures have one incompletely occupied Ag site, and structure Rb7Ag4.61Sc2.13(WO4)9 also contains two positions with mixed Ag and Sc. Both compounds contain ‘lanterns’ [M2(XO4)9] (M = (Sc, Ag), Sc; X = Mo, W), which are strengthened by three AgO2 dumbbells to give isolated building blocks [Ag3M2(XO4)9] forming two-story hexagonal layers resembling the structure of glaserite K3Na(SO4)2. Similar layers of [Ag3Sc2(WO4)9]9− building blocks were also found by us in the structure of Rb9–xAg3+xSc2(WO4)9, which is close to that of Rb9Ag3Sc2(MoO4)9. Similar layers of the [M2(TO4)9] units were also observed in Cs7Na5Yb2(MoO4)9 and Na13Sr2Ta2(PO4)9. The title compounds belong to the series of rhombohedral triple molybdates and tungstates with a ≈ 9–10 Å and large c-periods (more than 20 Å), which have layered or open 3D framework structures. Like many compounds of this series, Rb7Ag5Sc2(XO4)9 (Х = W, Mo) at elevated temperatures have significant ionic conductivity reaching values 6.1·10−3 S cm−1 at 703 K (X = Mo) and 1.4·10−3 S cm−1 at 733 K (X = W) with Еа = 0.7 eV and 0.6 eV, respectively.
Смотреть статью,
Scopus,
WOS,
Для получение полного текста обратитесь в библиотеку
Держатели документа: Baikal Institute of Nature Management, Siberian Branch, Russian Academy of Sciences, Sakh'yanova St. 6, Buryat Republic, Ulan-Ude, 670047, Russian Federation
Nikolaev Institute of Inorganic Chemistry, Siberian Branch, Russian Academy of Sciences, Akad. Lavrentyev Ave. 3, Novosibirsk630090, Russian Federation
Kirensky Institute of Physics, Federal Research Center KSC SB RAS, Akademgorodok 50 bld.38, Krasnoyarsk, 660036, Russian Federation
Kemerovo State University, Krasnaya St., 6, Kemerovo, 650000, Russian Federation
Skolkovo Institute of Science and Technology, Moscow121205, Russian Federation
Доп.точки доступа: Spiridonova, T. S.; Solodovnikov, S. F.; Molokeev, M. S.; Молокеев, Максим Сергеевич; Solodovnikova, Z. A.; Savina, A. A.; Kadyrova, Y. M.; Sukhikh, A. S.; Kovtunets, E. V.; Khaikina, E. G.