Аннотация: Silicon carbide 6H-SiC nanoparticles and nanowires were obtained in carbon-silicon high-frequency arc plasma plasma in a helium atmosphere at a pressure of 0.1-0.6 MPa. It was shown that 6H-SiC nanowires grow from the arc plasma, as well as from the vapor, according to the known mechanism of vapor-solid condensation on a cold surface covered with single-crystal silicon carbide nuclei. The content of silicon carbide nanowires in the condensate reached 60 wt %. The obtained single-crystal silicon 6H-SiC nanowires had the diameter of 15-18 nm and length of 200-600 nm.
Смотреть статью,
Scopus,
WOS,
Для получение полного текста обратитесь в библиотеку
Держатели документа:
Russian Acad Sci, Siberian Branch, LV Kirensky Phys Inst, Krasnoyarsk 660036, Russia
Siberian Fed Univ, Krasnoyarsk 660041, Russia
Russian Acad Sci, Siberian Branch, Krasnoyarsk Sci Ctr, Krasnoyarsk 660036, Russia
Доп.точки доступа:
Glushchenko, G. A.; Глущенко, Гарий Анатольевич; Leonova, T. A.; Kolonenko, A. L.; Колоненко, Андрей Леонидович; Dudnik, A. I.; Дудник, Александр Иванович; Osipova, I. V.; Осипова, Ирина Владимировна; Vnukova, N. G.; Внукова, Наталья Григорьевна; Nemtsev, I. V.; Немцев, Иван Васильевич; Zharkov, S. M.; Жарков, Сергей Михайлович; Churilov, G. N.; Чурилов, Григорий Николаевич