/ I. P.
Aleksandrova [et al.]> // Functional Materials. - 2010. -
Vol. 17,
Is. 1. - P. 18-23
. - ISSN 1027-5495
Аннотация: The heat capacity of NaNb1_xTaxO3 solid solutions was measured in the temperature range 100 to 770 K. The step-like change of phase transition temperature is observed in the T-x phase diagram at concentration x = 0.55. The obtained results are in a good agreement with the data of dielectric studies. The 23Na MAS NMR spectra were obtained at Larmor frequency 79.35 MHz using a Bruker AVANCE 300 spectrometer. The quadru-polar coupling constant, (CQ=e2qQ/h) and asymmetry parameter (n) were determined by computer fitting of the NMR line shape using the DMFit software. The found parameters show that solid solution structure is NaTa03-based at 0.7<X ?1 and NaNbO3-based at 0?x?0.5. The spectra in the intermediate region (0.5<x?0.7) can be described at a reasonable accuracy when assuming the coexistence of NaTaO3 and NaNbO3 structures. В© 2010 - STC "Institute for Single Crystals".
Scopus Держатели документа: L. V. Kirensky Institute of Physics, Russian Academy of Sciences, Siberian Branch, 660036 Krasnoyarsk, Russian Federation
Siberian Federal University, 660041 Krasnoyarsk, Russian Federation
Доп.точки доступа: Aleksandrova, I. P.; Александрова, Инга Петровна; Ivanov, Y. N.; Иванов, Юрий Николаевич; Bondarev, V. S.; Бондарев, Виталий Сергеевич; Sukhovskii, A. A.; Суховский, Андрей Андреевич; Voronov, V. N.; Воронов, Владимир Николаевич