1.
|
Вид документа : Статья из журнала Шифр издания :
Автор(ы) : Kashkina L. V., Stebeleva O. P., Emelyanova T. Y., Petrakovskaya E. A., Bayukov O. A.
Заглавие : Hydrodynamic dispersion of calcium aluminosilicate from technogenic and nonmetallic material
Место публикации : J. Sib. Fed. Univ. Eng. Technol. - 2014. - Vol. 7, Is. 1. - P.3-12; Журн. СФУ. Сер. "Техника и технологии"
Ключевые слова (''Своб.индексиров.''): hydrodynamic dispersion--cavitation--crystal ceramic foam--porous glass material--гидродинамическое диспергирование--кавитация--зола--пеноматериал--пористая стеклокерамика Аннотация: Physicochemical properties of two calcium aluminosilicate materials after reducing in the hydrodynamic rotary generator in supercavitation mode were studied. The samples are the crystal ceramic foam based on Kansko-Achinsk lignite-ash and the porous glass material obtained from low-manganese nonmetallic feed. X-ray phase analysis, EPR-method, NPR-method (the Mossbauer Effect) and optical microscopy were used. It was found that the material is changing its stucrure in a hydrodynamic dispersion process caused by high-cavitation. The nature of the changes depends on its initial state.Изучены физико-химические свойства двух кальций-алюмосиликатных материалов после измельчения в гидродинамическом генераторе роторного типа в режиме суперкавитации. Исследованы образцы – кристаллическая пенокерамика на основе зол бурых Канско-Ачинских углей и пористый стекломатериал, полученный из нерудного сырья с низким содержанием марганца. Для анализа были использованы методы РФА, ЭМР, ЯГР (эффект Мёссбауэра), оптическая микроскопия. Показано, что в процессе гидродинамического диспергирования за счет высокоэнергетического кавитационного воздействия в материалах происходят глубокие структурные изменения. Получено, что характер изменений зависит от исходного состояния исследуемого материала.
Смотреть статью, Читать в сети ИФ Найти похожие
|