Вид документа : Статья из журнала
Шифр издания :
Автор(ы) : Myagkov V. G., Bykova L. E., Zhigalov V. S., Tambasov I. A., Bondarenko G. N., Matsynin A. A., Rybakova A. N.
Заглавие : Solid-state synthesis, structural and magnetic properties of CoPd films
Коллективы : Russian Foundation for Basic Research [15-02-00948]
Место публикации : Phys. Solid State: MAIK Nauka-Interperiodica / Springer, 2015. - Vol. 57, Is. 5. - P.1014-1022. - ISSN 1063, DOI 10.1134/S1063783415050236. - ISSN 10906460(eISSN)
Примечания : Cited References:57. - This study was supported in part by the Russian Foundation for Basic Research (project no. 15-02-00948).
Предметные рубрики: HIGH-TEMPERATURE SYNTHESIS
EPITAXIAL THIN-FILMS
CENTERED-CUBIC CO
MARTENSITIC TRANSFORMATIONS
PHASE SYNTHESIS
SINGLE-CRYSTAL
FE FILMS
CO/PD MULTILAYERS
RECORDING MEDIA
ANISOTROPY
Аннотация: The results of the investigation of the structural and magnetic properties of CoPd films with equiatomic composition have been presented. The films have been synthesized by vacuum annealing of polycrystalline Pd/Co and epitaxial Pd/α-Co(110) and Pd/β-Co(001) bilayer samples. It has been shown that, for all samples, the annealing to 400°C does not lead to the mixing of layers and the formation of compounds. A further increase in the annealing temperature results in the formation of a disordered CoPd phase at the Pd/Co interface, which is fully completed after annealing at 650°C. The epitaxial relationships between the disordered CoPd phase and the MgO(001) substrate are determined as follows: CoPd(110)〈1¯11|| MgO(001)〈100〉 and CoPd(001)[100] || MgO(001)[100], which are formed in the Pd/αCo(110) and Pd/βCo(001) films, respectively. According to the calculations, the first magnetocrystalline anisotropy constants of the disordered CoPd phase for Pd/αCo(110) and Pd/βCo(001) samples have close values: = –(1.6 ± 0.4) × 105 erg/cm3. A possible mechanism of the solidstate synthesis of the CoPd alloy is proposed.