A highly efficient and suitable spectral profile Cr3+-doped garnet near-infrared emitting phosphor for regulating photomorphogenesis of plants / X. Zou, X. Wang, H. Zhang [et al.] // Chem. Eng. J. - 2022. - Vol. 428. - Ст. 132003, DOI 10.1016/j.cej.2021.132003. - Cited References: 46. - The work was supported from the National Natural Science Foundations of China (Nos. 21671070, 51802101), the Guangdong Basic and Applied Basic Research Foundation (No. 2021A1515012613), the Guangdong Provincial Science & Technology Project (Nos. 2020A1414010046, 2021A0505050006), the Guangzhou Science & Technology Project (No. 202007020005), the Natural Science Foundation of Guangdong Province (No. 2018A030310217), the Project of GDUPS (2018) for Prof. Bingfu LEI, and the Guangdong Provincial Special Fund for Modern Agriculture Industry Technology Innovation Teams (Nos. 2021KJ131 , 2021KJ122)
. - ISSN 1385-8947
Перевод заглавия: Высокоэффективный и подходящий спектральный профиль гранатового люминофора ближнего инфракрасного диапазона, легированного Cr3+, для регулирования фотоморфогенеза растений
Кл.слова (ненормированные):
Cr3+-doped phosphor -- NIR pc-LED -- Photomorphogenesis -- Plant growth
Аннотация: Far-red/phytochrome (PFR) plays a key role in photomorphogenesis of plants. However, how to obtain a near-infrared (NIR) emitting phosphor with high external quantum efficiency (EQE), suitable spectral profile, and low thermal quenching remains a huge challenge. Herein, a NIR phosphor, Gd2.4Lu0.6Ga4AlO12:Cr3+,H3BO3 (GLGA:Cr3+) was developed via regulating the crystal field environment and adding fluxes, which exhibits a peak maximum at 728 nm with a relatively narrow full-width at half maximum (FWHM) of 107 nm, matching well with the absorption band of PFR. Upon 450 nm excitation, the internal quantum efficiency (IQE) and EQE of the optimal phosphor are 90.3% and 32.0%, respectively. At 423 K, the integrated emission intensity of the investigated phosphor is about 75% of that at room temperature. Benefiting from the excellent optical performance, a NIR phosphor-converted light-emitting diode (pc-LED) was fabricated, which shows a NIR output power of 505.99 mW and photoelectric conversion efficiency of 11.24% at 300 mA. Moreover, plant growth experiments demonstrate that the biomass of pea seedlings is increased by 67.72% under supplementary NIR light irradiation. The findings of this research will motivate further research on new Cr3+-doped NIR phosphors for regulating photomorphogenesis of plants.
Смотреть статью,
Scopus,
WOS,
Читать в сети ИФ
Держатели документа:
Key Laboratory for Biobased Materials and Energy of Ministry of Education, College of Materials and Energy, South China Agricultural University, Guangdong, Guangzhou, 510642, China
Maoming Branch, Guangdong Laboratory for Lingnan Modern Agriculture, Guangdong, Maoming 525100, China
Department of Physics, Georgia Southern University, Statesboro, GA 30460, United States
College of Horticulture, South China Agricultural University, Guangzhou, 510642, China
SB RAS, Kirensky Inst Phys, Lab Crystal Phys, Krasnoyarsk, 660036, Russian Federation
Доп.точки доступа:
Zou, X.; Wang, X.; Zhang, H.; Kang, Y.; Yang, X.; Zhang, X.; Molokeev, M. S.; Молокеев, Максим Сергеевич; Lei, B.
}
Найти похожие
|
Главная
Каталог книг и брошюр библиотеки ИФ СО РАН
Стандартный
Центральная Научная Библиотека КНЦ СО РАН