    Structural phase transformation and luminescent properties of Ca2-xSrxSiO4:Ce3+ orthosilicate phosphors / M. Chen [et al.] // Inorg. Chem. - 2015. - Vol. 54, Is. 23. - P. 11369-11376, DOI 10.1021/acs.inorgchem.5b01955. - Cited References: 38. - The present work was supported by the National Natural Science Foundations of China (Grant Nos. 51572023, 51272242, and 51511130035), Natural Science Foundations of Beijing (2132050), the Program for New Century Excellent Talents in Univ. of Ministry of Education of China (NCET-12-0950), Beijing Nova Program (Z131103000413047), Beijing Youth Excellent Talent Program (YETP0635), and the Funds of the State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences (RERU2015022) . - ISSN 0020-1669
   Перевод заглавия: Структурный фазовый переход и люминесцентные свойства ортосиликата Ca2-xSrxSiO4:Ce3+

РУБ Chemistry, Inorganic & Nuclear
Рубрики:
LIGHT-EMITTING-DIODES
   DICALCIUM SILICATE
   CRYSTAL-STRUCTURE
   SOLID-SOLUTION
   BOND-VALENCE
   Ce3+
   Eu2+
   β-Ca2SiO4
   GREEN
   TEMPERATURE
Аннотация: The orthosilicate phosphors demonstrate great potential in the field of solid-state lighting, and the understanding of the structure-property relationships depending on their versatile polymorphs and chemical compositions is highly desirable. Here we report the structural phase transformation of Ca2-xSrxSiO4:Ce3+ phosphor by Sr2+ substituting for Ca2+ within 0 ≤ x 2. The crystal structures of Ca2-xSrxSiO4:Ce3+ are divided into two groups, namely, β phase (0 ≤ x 0.15) and α′ phase (0.18 ≤ x 2), and the phase transition (β → α′) mechanism originated from the controlled chemical compositions is revealed. Our findings verified that the phase transition Pnma (α′-phase) ↔ P21/n (β-phase) can be ascribed to the second-order type, and Sr2+ ions in Ca2-xSrxSiO4 preferentially occupy the seven-coordinated Ca2+ sites rather than the eight-coordinated sites with increasing Sr2+ content, which was reflected from the Rietveld refinements and further clarified through the difference of the Ca-O bond length in the two polymorphs of Ca2SiO4. The emission peaks of Ce3+ shift from 417 to 433 nm in the composition range of 0 ≤ x ≤ 0.8, and the difference in the decay curves can also verify the phase transformation process. Thermal quenching properties of selected Ca2-xSrxSiO4:Ce3+ samples were evaluated, and the results show that the integral emission intensities at 200 °C maintain 90% of that at room temperature suggesting superior properties for the application as white light-emitting diodes (w-LEDs) phosphors. © 2015 American Chemical Society.

Смотреть статью,
Scopus,
WOS,
Читать в сети ИФ
Держатели документа:
School of Materials Sciences and Engineering, University of Science and Technology Beijing, Beijing, China
Laboratory of Crystal Physics, Kirensky Institute of Physics, SB RAS, Krasnoyarsk, Russian Federation
Department of Physics, Far Eastern State Transport University, Khabarovsk, Russian Federation

Доп.точки доступа:
Chen, M.; Xia, Z.; Molokeev, M. S.; Молокеев, Максим Сергеевич; Liu, Q.
Свободных экз. нет}
Найти похожие