Synthesis, structure and photoluminescent properties of Eu:Gd2O3 nanophosphor synthesized by cw CO2 laser vaporization / A. I. Kostyukov, V. N. Snytnikov, V. N. Snytnikov [et al.] // J. Lumines. - 2021. - Vol. 235. - Ст. 118050, DOI 10.1016/j.jlumin.2021.118050. - Cited References: 42. - The TEM studies are conducted using the equipment of the Center of Collective Use « National Center of Catalyst Research». This work is financially supported by the Russian Foundation for Basic Research (RFBR), Project no. 19-32-60027
. - ISSN 0022-2313
Кл.слова (ненормированные):
Photoluminescence -- Eu3+ ions -- Monoclinic Gd2O3 -- Nanophosphors -- Laser vaporization
Аннотация: Europium doped Gd2O3 sphere-like nanoparticles with dm = 9.3 ± 3.5 nm were synthesized by cw CO2 laser vaporization technique in a flowing mixture of argon and oxygen. According to XRD data, the Eu:Gd2O3 nanoparticles crystallize in the monoclinic symmetry class (C2/m space group). High-resolution luminescence spectroscopy study showed that the ultra-narrow 5D0 → 7F0 transition of Eu3+ demonstrates only two peaks corresponding to two inequivalent Cs positions of Eu3+ ion in monoclinic Gd2O3 lattice that is explained by the peculiarities of local environment of Eu3+ ion at these sites. The hypersensitive transition 5D0 → 7F2 dominates in the spectrum and is expanded to the red part of the spectrum in comparison with cubic Eu:Gd2O3 due to intense transitions terminating at higher-lying components of the crystal-field-split 7F2 state. In the luminescence spectrum, an additional weak band with the maximum at 407 nm corresponding to the electronic transitions 4f65 d1(7FJ) → 4f7(8S7/2) of Eu2+ was detected. The obtained values of chromaticity coordinates and absolute quantum yield are (0.644; 0.325) and ca. 1%, respectively. The phase transformations have been investigated using differential scanning calorimetry and thermogravimetry (50–1400 °C). After annealing in air at 700 °C, the monoclinic symmetry class of the Eu:Gd2O3 nanoparticles is preserved and the particle size increases to dm = 17.8 ± 6.1 nm. After annealing, the chromaticity coordinates (0.659; 0.334) and absolute quantum yield (ca. 4%) can be obtained using red phosphor based on monoclinic Gd2O3:Eu3+. The lifetime of the excited 5D0 state of Eu3+ in the annealed nanoparticles is longer than that in the as-synthesized nanoparticles, due to the suppression of nonradiative decay after annealing.
Смотреть статью,
Scopus,
WOS,
Читать в сети ИФ
Держатели документа:
Novosibirsk State University, Pirogova Str. 2, Novosibirsk, 630090, Russian Federation
Boreskov Institute of Catalysis SB RAS, Lavrentieva Ave. 5, Novosibirsk, 630090, Russian Federation
Nikolaev Institute of Inorganic Chemistry SB RAS, Akad. Lavrentiev Ave. 3, Novosibirsk, 630090, Russian Federation
Institute of Laser Physics SB RAS, Lavrentyev Ave. 15b, Novosibirsk, 630090, Russian Federation
Novosibirsk State Technical University, K. Marx Ave. 20, Novosibirsk, 630073, Russian Federation
Kirensky Institute of Physics Federal Research Center KSC SB RAS, Krasnoyarsk, 660036, Russian Federation
Department of Photonics and Laser Technology, Siberian Federal University, Krasnoyarsk, 660041, Russian Federation
Доп.точки доступа:
Kostyukov, A. I.; Snytnikov, V. N.; Rakhmanova, M. I.; Kostyukova, N. Y.; Ishchenko, A. V.; Cherepanova, S. V.; Krylov, A. S.; Крылов, Александр Сергеевич; Aleksandrovsky, A. S.; Александровский, Александр Сергеевич
}
Найти похожие
|
Главная
Каталог книг и брошюр библиотеки ИФ СО РАН